Awards Nomination 20+ Million Readerbase
Indexed In
  • Open J Gate
  • Genamics JournalSeek
  • Academic Keys
  • JournalTOCs
  • ResearchBible
  • China National Knowledge Infrastructure (CNKI)
  • Scimago
  • Ulrich's Periodicals Directory
  • Electronic Journals Library
  • RefSeek
  • Hamdard University
  • EBSCO A-Z
  • OCLC- WorldCat
  • SWB online catalog
  • Virtual Library of Biology (vifabio)
  • Publons
  • MIAR
  • Scientific Indexing Services (SIS)
  • Euro Pub
  • Google Scholar
Share This Page
Journal Flyer
Journal of Nanomedicine & Nanotechnology
Characterization of nanobiocomposite functionally graded YSZ/HAP prepared by electrophoretic deposition for biomedical applications
19th International Conference on Nanotechnology and Expo
November 13-14, 2017 | Atlanta, USA

Makarim Hazim Abdulkareem, Muhammad Jasim Kadhim and Nawal Ezat

University of Technology, Iraq

Posters & Accepted Abstracts: J Nanomed Nanotechnol

Abstract:

This work describes preparation functionally graded coating of YSZ/HAP on stainless steel 316L as a substrate via electrophoretic deposition. Four layers (100%YSZ), (70% YSZ+30% HAP), (30% YSZ+70% HAP) and (100% HAP) were deposited on thin layer of chitosan. Also nano particles of chitosan were used as a binder material in all (FGMs) layers instead of sintering step. Ethanol with 5% deionized water was used as a suspension for deposition procedure, pH value performed at 4 which fitted by using acetic acid. Four parameters were used in EPD procedure (time, voltage, concentration and temperature) Stability of solutions was measured by zeta potential that showed the high value of zeta potential for FGMs solution than the solution of single layer. The microstructure of surface coating and thickness of layers were characterized by optical microscopy and SEM that showed homogeneity and crack free. Thickness of single and FGM layers that obtained is varied between (12-85 µm). Hydrophilicity property was investigated by wettability test which the result showed the super hydrophilicity for FGMs as compared with single coating layer.